BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush

Basic Information
Place of Origin: Jiangsu, China
Brand Name: BPT
Model Number: 02A01
Minimum Order Quantity: 50 Pieces
Price: $1.00/Pieces >=1 Pieces
Supply Ability: 10000 Piece/Pieces per Month
Detail Information
Type: Ceramic Parts Application: Structure Ceramic, Industrial Equipment
Material: Zirconia Ceramic, Engineering Ceramics Processing Service: Custom Processing
Product Name: Precision Ceramic Parts Size: Customized Size
Drawing Format: 2D/(PDF/CAD)3D(IGES/STEP) Quality Control: 100% Inspection
Port: Shenzhen Or Hong Kong
High Light:

BPT Zirconia Ceramics Bolts

,

BPT Zirconia Ceramics Screws

,

BPT zirconia ceramic bush


Product Description

Zirconia ceramic parts customization, high-precision ceramic parts, engineering ceramic structural parts
 

 

 

We manufactures custom technical ceramic parts and components, covering a wide range of customer reuquirements. We make use of several forming and machining techniques to process components made from alumina, zirconia, cordierite. These materials may be used in applications that require wear or coorosion resistance. High temperature capability, or ceramic insulators for electrical resistance.

 

Zirconia Ceramic Performance Table
Property
Item
Data
Unit
 
 
 
 
 
 
Mechanical Characteristics
Color
Ivory -
Density
6.02
g/cm3
Bending Strength
800
MPa
Compressive trength
3000
MPa
Elastic Modulus
200
GPa
Fracture Toughness
8
MPa m1/2
Weber Coefficient
15
m
Vickers Hardness
1200
HV 0.5
 
 
Thermal Characterics
Coefficient of Line Thermal Expansion
10
10-6K-1
Thermal Conductivity
3
W/mK
Thermal Shock Resistance(Put in Water)
300
ΔT °C
Max Working Temperature
1000
°C
 
 
Electrical Characteristics
Volume Resistance at 20°C
>1013
Ωcm
Dielectric Strength
11×106
V/m
Dielectric Constant
33
εr
One MHZ Dielectric Loss Angle at 20°C
0.0016
tanδ
 
Chemical Characteristics
Nitric Acid (60%) 90°C
≒0.00
 
WT Loss mg/cm^2/day
Sulphuric Acid (95%) 95°C
0.04
Caustic Soda (30%) 80°C
0.08
 
What Can We Do
We can provide a variety of high-performance engineering ceramics.
BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush 0

Silicon Nitride Ceramics (Si3N4)

Silicon nitride exceeds other ceramics in thermal shock resistance. Its strength does not deteriorate at elevated temperatures, hence it is most appropriate for engine and gas turbine parts, including turbo charger rotors, diesel engine glow plugs and hot plugs.
BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush 1

Alumina Ceramics (Al2O3)

Alumina is the most widely used type of ceramic. Its high dielectric properties are beneficial in electrical products, Alumina offers corrosion and wear resistance and high strength. It is widely used for industrial machine parts.
BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush 2

Silicon Carbide Ceramic (SiC)

Silicon carbide retains its strength at elevated temperatures as high as 1400℃. It has the highest corrosion resistance of all fine ceramic materials. Applications include mechanical seals and pump parts.
BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush 3

Zirconia Ceramics (ZrO2)

Zirconia ceramic has the highest strength and toughness at room temperature of all engineering ceramics. Before zirconia, ceramics were considered impractical for scissor or knife applications. With its excellent surface smoothness, zirconia is also used for pump parts.
BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush 4

Aluminum Nitride Ceramics(AIN)

Aluminum nitride ceramics are usually gray or off-white. It has a low thermal expansion coefficient, excellent insulation performance, heat resistance, and a thermal conductivity of more than 180W/(m.k). It is an ideal package heat dissipation material for large integrated circuits.
BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush 5

Machinable Glass Ceramic

Machinable glass ceramics are fluorophlogopite mica glass ceramics with synthetic mica as the main crystal phase. The main components are fluorophlogopite and glass with silica as the main component. Contains 55% fluorophlogopite and 45% borosilicate glass matrix.
BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush 6

Microporous Ceramic Plate

Microporous ceramics refer to ceramic bodies containing a large number of open or closed tiny pores. The material is mainly alumina or carbonized. The surface is firm, the pores are uniform, the porosity is 35-40%, and the pore size ranges from 1 to 100 microns.
BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush 7

Boron Nitride(h-BN)

Boron nitride material has the characteristics of resistance to high temperature and heat cycle. It will not react with many metals, ceramic rare earths and other materials, nor will it contaminate the product. Will not break in hot and cold environments.
BPT Zirconia Ceramics Parts Bolts Screws Ball Mill Grinding Jars Guide Bush 8

Other Ceramics

Our company can process a variety of ceramic materials and cemented carbide. We are currently processing experimental splines for many research institutes and schools. You can provide materials and we can process them according to drawings.
 
 
 
 
 
 